Jotun Marathon 550 Tds

Jotun Marathon 550 Tds

A (base) to be mixed thoroughly with 1 part marathon 500, comp. b (curing agent) induction time 10 minutes. pot life (23°c) 1. 5 hour (reduced at higher temperatures) thinner/cleaner jotun thinner no. 17 guiding data airless spray pressure at nozzle 17 mpa (170 kp/cm², 2500 psi) nozzle tip 0. 53 0. 69 mm (0. 021-0. 027″) spray angle 40 80°. jotun marathon 550 tds Marathon550. marathon550 is a high build, highly abrasion resistant, surface tolerant two component epoxy coating. it is ideally suited for structures exposed to harsh environments and require an extra solid barrier to its surroundings. in particular those in the subsea, splashor tidal zones. Technical data marathon iq product description marathon iq is a practically solvent free, abrasion resistant, two-pack epoxy coating. recommended use steel subject to exstreme mechanical exposure such as underwater areas of ice going vessels including ice breakers. certificate: ice class: recognised low friction surface coating (lr).

Jotunmarathon550 Marine Steel Concrete Primer

Jotun marathon 500 is a two component polyamine cured epoxy coating that is a surface tolerant, high solids, high build product. this product will continue to cure when immersed in water and has high abrasion resistance. Marathon 550 allows for up to 550 microns in one coat, is applicable on hydroblasted and slightly damp surfaces and will continue to cure under water shortly after application. suitable jotun marathon 550 tds for both maintenance and new construction. wide range of colours are available through jotun’s multicolor industry system. Tds marathon iq english. 4 pages. tds mammut topcoat english. 3 pages. tds mammut primer english. 3 pages. tds jotun thinner no. 2 english. 3 pages. tds jotun thinner no. 17 english. 2 pages. balloxy hb lumi. 4 pages. jotaguard 600 series. 12 pages. hardtop topcoat. 12 pages. jotamastic.

Technical Data Sheets Benjamin Moore

The information in this document is given to the best of jotun’s knowledge, base on laboratory testing and practical experience. jotun’s products are considered as semi-finished goods and as such, product are often used under conditions beyond jotun’s control. jotun cannot guarantee anything but the quality of the product itself. Marathon550 product description this is a two component polyamine cured epoxy coating. it is a surface tolerant product that can be applied on moist substrates. will continue to cure when immersed in water. the product has high abrasion resistance. suitable for environments with very high corrosivity, such as areas in the splash or tidal zone. The technical data sheet (tds) is recommended to be read in conjunction with the safety data sheet (sds) and the application guide (ag) for this product. for your nearest local jotun office, please visit our website at www. jotun. com. open the catalog to page 1. Marathon550 comp a 4part(s) marathon 550 comp b 1part(s) thinner/cleaning solvent thinner: jotun thinner no. 17 nozzle tip (inch/1000): pressure at nozzle (minimum): guiding data for airless spray 21-27 170 bar / 2500 psi drying and curing time surface (touch) dry walk-on-dry 15 h11 h9 h4 h1. 5 h 26 h18 h14 h8 h3 h 14 d10 d10 d7 d3 d.

Technical Data Sheets Benjamin Moore

Sigmadur 550 h is a two-component, high solids, high-build aliphatic acrylic polyurethane finish. additional product benefits. excellent resistance to atmospheric exposure conditions. good colour and gloss retention. cures at temperatures down to -5°c (23°f). A (base) to be mixed thoroughly with 1 part marathon, comp. b (curing agent) pot life (23°c) 1 hour (reduced at higher temperatures) thinner/cleaner jotun thinner no. 17. guiding data airless spray. pressure at nozzle 15 mpa (150 kp/cm², 2100 psi) nozzle tip 0. 63 1. 09 mm (0. 025-0. 043″) spray angle 65 80° filter filters to be removed. Tds marathon iq english 4 pages. add to mynauticexpo favorites (85 130 µm, ry5) (iso 8503-2). other surfaces the coating may be used on other substrates. please contact your local jotun office for more information. condition during application the temperature of the substrate should be minimum 10°c and at least 3°c above the dew.

Please contact your local jotun office for more information. condition during application the temperature of the substrate should be minimum 3ºc above the dew point of the air, temperature and relative humidity measured in the vicinity of the substrate. tds marathon iq english. 4 pages. tds mammut topcoat english. 3 pages. tds.

Sigmadur New Guard Coatings

She dept. jotun as, norway +47 33 45 70 00 jotun uae ltd. l. l. c. p. o. box 3671, dubai, u. a. e. tel: 009714 3395000 fax:009714 3380666 jotun abu dhabi l. l. c. p. o. box-3714 abu dhabi u. a. e. tel: 00971 2 5510300 fax:00971 2 5510232 [email protected] com section 2. hazards identification flammable liquids category 3 skin corrosion/irritation category 2. Cabinet coat trim & cabinet enamel satin finish cc-45xx cabinet coat trim & cabinet enamel semi-gloss finish cc-46xx cabinet coat trim & cabinet enamel satin finish cc-55xx cabinet coat trim & cabinet enamel semi-gloss finish cc-56xx century small batch interior paint 030 chlorinated rubber swimming pool paint semi-gloss finish cr-26xx clean, multi purpose jotun marathon 550 tds cleaner n318 clearcoat pro ht.

Marathon550 is a high build, highly abrasion resistant, surface tolerant two component epoxy coating. it is ideally suited for structures exposed to harsh environments and require an extra solid barrier to its surroundings. in particular those in the subsea, splashor tidal zones. marathon 550 allows for up to 550 microns in one coat,. A (base) to be mixed thoroughly with 1 part marathon 500, comp. b (curing agent) induction time 10 minutes. pot life (23°c) 1. 5 hour (reduced at higher temperatures) thinner/cleaner jotun thinner no. 17. guiding data airless spray. pressure at nozzle 17 mpa (170 kp/cm², 2500 psi) nozzle tip 0. 53 0. 69 mm (0. 021-0. 027″) spray angle 40 80°. Jotun worldwide germany jotun (deutschland) gmbh haferweg 38 22769 hamburg tel: +49 40 851 960 fax:+49 40 856 234 australia jotun australia pty. ltd. p. o. box 105, altona north, 9 cawley road, brooklyn, vic 3025 tel: +61 3 9314 0722 fax: +61 3 9314 0423 great britain jotun paints (europe) ltd. stather road, flixborough, scunthorpe dn15 8rr tel.

The sigmadur range is an innovative selection of finish products that meet the demands for long-lasting and highly resilient systems within aggressive environments. full range of colours. varying gloss levels. proven track record in protecting onshore and offshore structures. offers atmospheric, abrasion and corrosion resistance. can cure down to -5°c. meets and exceeds the highest. Jotunmarathon550 is a two component polyamine cured epoxy coating for jotun marathon 550 tds carbon steel, galvanised, stainless steel, aluminium and concrete substrates as a primer, mid coat, finish coat or as single coat system in atmospheric and immersed environments. recommended for use in offshore environments, refineries, power plants, bridges, buildings, mining equipment and general structural steel. Marathon 500 product description this is a two component polyamine cured epoxy coating. it is a surface tolerant, high solids, high build product. according to jotun performance coatings’ definition. calculated all data is valid for mixed paint. (tds) is recommended to be read in conjunction with the safety data sheet (sds) and the. Marathon550 is surface tolerant for early immersion, and can be applied on damp surfaces. it is high build and abrasion resistant, low voc and made for efficient application. • high solids, high build abrasion resistant epoxy coating jotun a/s p. o box 2021 n-3202 sandefjord.

Marathon 550 comp a 4part(s) marathon 550 comp b 1part(s) thinner/cleaning solvent thinner: jotun thinner no. 17 nozzle tip (inch/1000): pressure at nozzle (minimum): guiding data for airless spray 21-27 170 bar / 2500 psi drying and curing time surface (touch) dry walk-on-dry 15 h11 h9 h4 h1. 5 h 26 h18 h14 h8 h3 h 14 d10 d10 d7 d3 d. Satin impervo® alkyd low lustre enamel (regional special, see tds) z235 satin impervo® alkyd low lustre jotun marathon 550 tds enamel c235 seal lock® plus interior alcohol based primer sealer il-6800 semi-transparent deck & siding stain m7600 series solid color 100% acrylic deck stain m8500 series solvents 1a. xxx spar varnish 1v. 109 spark’len clean floor cleaner.

Marathon550 comp b 3. 6 marathon 550 comp a 14. 4 20 5 storage volume (liters) date of issue:7 january 2020 page: 4/5 this technical data sheet supersedes those previously issued. the technical data sheet (tds) is recommended to be read in conjunction with the safety data sheet (sds) and the application guide (ag) for this product. Technical data sheet jotafix epoxy primer jotafix epoxy primer comp a jotafix epoxy primer comp b product mixing ratio (by volume) 5 part(s) 1 part(s)thinner/cleaning solvent thinner: jotun thinner no. 17 pressure at nozzle (minimum): 150 bar / 2100 psi dry to over coat, minimum 40 h 30 h 15 h 8 h 4 h 1. 5 h for maximum overcoating intervals, refer to the application guide (ag) for this product. Marathon 550. marathon 550 is a high build, highly abrasion resistant, surface tolerant two component epoxy coating. it is ideally suited for structures exposed to harsh environments and require an extra solid barrier to its surroundings. in particular those in the subsea, splashor tidal zones.